Détails sur le produit:
|
| Emballer: | Boîte de carton | Changement linéaire permanent: | Pour les appareils de traitement des eaux usées, la température maximale est de 1400 °C*3h±0.5 |
|---|---|---|---|
| Expérience: | 30 ans | Résistance chimique: | Haut |
| Absorption de l'humidité: | Faible | résistance à la flexion: | >20MPa |
| Couleur: | Blanc à gris clair | CCS Force: | 45 |
| Type de brique: | Réfractaire | Résistance à la flexion: | Haut |
| Réfractarité sous charge: | 1740 | Taux linéaire de changement: | ≤0,2% |
| Résistance aux chocs: | Haut | Porosité apparente: | 24 |
| Forme: | Taille de brique standard ou personnalisée | ||
| Mettre en évidence: | high alumina refractory brick for kilns,acid resistant refractory bricks,fire-resistant bricks for industrial furnaces |
||
High Alumina Brick Features
1.Refractoriness:
The refractoriness of high aluminum brick is higher than that of clay brick and semi-silicon brick, up to 1750~1790℃, which is a high-grade refractory material.
2.Refractoriness Under Load:
Because the Al2O3 in high aluminum products is high, the impurity is less, the formation of fusible glass body is less, so the load softening temperature is higher than that of clay bricks.
3.Slag Resistance:
There are more Al2O3 in high aluminum bricks, close to neutral refractory materials, which can resist the erosion of acidic slag and alkaline slag.
High Alumina Bricks Application
1.Used for masonry lining of steel making furnaces,glass furnaces ,cement rotary furnaces.
2. Used for blast stoves , electric furnace tops , for hot blast stoves , electric furnace tops ,blast furnaces , reverberatory furnaces ,rotary kiln linings.
3. High alumina bricks can also be processed into open hearth regenerative grid bricks, socket bricks for pouring system, nozzle bricks, etc. according to the requirements of industrial furnaces.
High Alumina Refractory Brick Physical and Chemical Index:
| Item/Grade | Fire Clay Brick | High Alumina Brick | ||||||
| SK-30 | SK-32 | SK-34 | SK-35 | SK-36 | SK-37 | SK-38 | SK-40 | |
| AL2O3% (≥) | 30 | 35 | 38 | 45 | 55 | 65 | 70 | 82 |
| Fe2O3% (≤) | 2.5 | 2.5 | 2 | 2 | 2 | 2 | 2 | 2 |
| Refractoriness(SK) | 30 | 32 | 34 | 35 | 36 | 37 | 38 | 40 |
| Refractoriness Under Load, 0.2MPa, °C (≥) | 1250 | 1300 | 1360 | 1420 | 1450 | 1480 | 1530 | 1600 |
| Apparent Porosity (%) | 22-26 | 20-24 | 20-22 | 18-20 | 20-23 | 20-23 | 20-22 | 18-20 |
| Bulk Density (g/cm³) | 1.9-2.0 | 1.95-2.1 | 2.1-2.2 | 2.15-2.22 | 2.25-2.4 | 2.3-2.5 | 2.4-2.6 | 2.5-2.7 |
| Cold Crushing Strength ,MPa (≥) | 20 | 25 | 30 | 40 | 45 | 50 | 60 | 70 |
| Brick Standard Sizes | |||||
| SPLITSTRAIGHT L×W×H(mm) |
SPLIT L×W×H(mm) |
ARCH L×W×H(mm) |
WEDGE L×W×H(mm) |
TILE L×W×H(mm) |
OTHER SHAPE |
| 230×114×65 | 230×114×25 | 230×114×65/45 | 230×114×65/45 | 230×230×38 | Key brick |
| 230×114×75 | 230×114×32 | 230×114×65/55 | 230×114×65/55 | 230×230×50 | Skew brick |
| 230×114×37 | 230×114×75/45 | 220×114×75/45 | 230×230×65 | Soap | |
| 230×114×50 | 230×114×75/55 | 220×114×75/55 | 230×230×75 | Checker | |
| ≤10 | 230×114×75/65 | 220×114×75/65 | Neck | ||
| Taper | |||||
| Application | Steel furnace, glass furnace, sodium silicate furnace, ceramic shuttle kiln, cement rotary kiln, blast furnace, electric furnace,blast furnace and reverberatory furnace. | ||||
| We also can make brick according to customers’ drawing and requirements. |
|||||